Catalytic degradation of toxic organic dye using an aluminum-doped Cu0.4Zn0.6-xAlxFe2O4 (x = 0.0, 0.2, 0.4, 0.6) spinel ferrite in a photo-Fenton system

Catalytic activity of spinel ferrite in breaking down toxic dye materials are promising due to their uniqueness. In this study, aluminum-doped copper zinc ferrite, Cu_0.4Zn_0.6-xAl_xFe₂O₄ (x = 0.0, 0.2, 0.4, 0.6), a catalyst for toxic dye degradation is synthesized through chemical co-precipitation route. The formation of the spinel ferrite catalyst is initially confirmed by Fourier transform infrared spectra, which shows the frequency of metal-oxygen bond vibration at 539 and 427 cm⁻¹ attributed to the tetrahedral and octahedral sites respectively. Higher intensity sharp peak of X-ray diffraction for (311) plane is the evidence for the phase purity and the formation of spinel ferrite. The crystallite size is found to decrease with the increase of Al³⁺ ion. The surface structure of the obtained particles is investigated using a scanning electron microscope. Analyses of the material's magnetic characteristics using a vibrating sample magnetometer (VSM) revealed that it is, in fact, a soft magnet, as evidenced by the loop of its hysteresis, which is narrow. The catalytic degradation of methylene blue dye under the mechanism of the photo-Fenton process is studied with the obtained spinel ferrites and the result is found to be as high as 96.5%. The process follows pseudo-second order kinetics and the Langmuir isotherm.     

MoS_2/Bi_2S_3异质结光催化剂的制备及其光催化性能

以五水硝酸铋为铋源、钼酸钠为钼源、硫脲为硫源,采用简单的一步水热法合成了MoS_2/Bi_2S_3异质结光催化剂,采用XRD,SEM,TEM,BET,UV-Vis DRS技术对其进行了表征。表征结果显示,MoS_2纳米片在Bi_2S_3微棒表面生长,增加了比表面积和活性位点,并形成异质结构,促进了光生载流子的迁移,抑制了电子-空穴对的再复合。实验结果表明:钼酸钠与五水硝酸铋的质量比为1∶2时制备的复合光催化剂性能最好,反应180min时对亚甲基蓝的去除率可达96.4%,明显高于MoS_2和Bi_2S_3,且具有较高的稳定性;该催化剂对罗丹明B、甲基橙和4-硝基苯酚的去除率分别为97.1%、93.1%和90.5%,表明其对污染物具有普适性。     

Ammonium nitrate thermal decomposition with additives

Runaway reactions present a potentially serious threat to the chemical process industry and the community; such reactions occur time and time again often with devastating consequences. The main objective of this research is to study the root causes associated with ammonium nitrate (AN) explosions during storage. The research focuses on AN fertilizers and studies the effects of different types of fertilizer compatible additives on AN thermal decomposition. Reactive Systems Screening Tool (RSST) has been used for reactivity evaluation and to better understand the mechanisms that result in explosion hazards. The results obtained from this tool have been reported in terms of parameters such as “onset” temperature, rate of temperature and pressure rise and maximum temperature. The runaway behavior of AN has been studied as a solid and solution in water. The effect of additives such as sodium sulfate (Na₂SO₄) and potassium chloride (KCl) has also been studied. Multiple tests have been conducted to determine the characteristics of AN decomposition accurately. The results show that the presence of sodium sulfate can increase the “onset” temperature of AN decomposition thus acting as AN thermal decomposition inhibitor, while potassium chloride tends to decrease the “onset” temperature thus acting as AN thermal decomposition promoter.     

层状氧化物NaCo_2O_4热催化H_2O_2降解亚甲基蓝

采用固相烧结法制备了NaCo_2O_4催化剂,构建了NaCo_2O_4-H_2O_2热催化体系降解亚甲基蓝(MB)。XRD和SEM表征结果显示,合成的NaCo_2O_4催化剂具有良好的稳定性。NaCo_2O_4对H_2O_2具有良好的热催化性能,反应温度越高,反应速率常数k越大,该催化反应符合一级动力学方程。NaCo_2O_4-H_2O_2体系对MB具有较好的降解效果,在反应温度为50℃、NaCo_2O_4加入量为50 mg、MB溶液加入量为100 mL、MB初始质量浓度为30 mg/L、H_2O_2加入量为1.00 mL的最优条件下,反应340 min时,MB降解率达87.00%;催化剂重复使用三次,MB降解率仍可达85%以上;经捕获剂效果对比实验发现,催化反应体系中存在h~+、·OH等催化活性物种。     

石墨相氮化碳协同UV-H_2O_2光催化降解亚甲基蓝

以三聚氰胺为前驱体,经热解—回流法制备了石墨相氮化碳(g-C3N4),采用XRD、FTIR、SEM、EDS、PL等技术对g-C_3N_4进行了表征。研究了g-C_3N_4在UV-H_2O_2体系中对废水中亚甲基蓝(MB)的光降解效果。实验结果表明,UV+g-C_3N_4催化剂+H_2O_2体系能协同降解MB,在初始MB质量浓度为20 mg/L、初始废水p H为5、废水体积为250 mL、g-C_3N_4加入量为0.10 g、H_2O_2浓度为0.4 mmol/L、反应温度为25℃的优化工艺条件下,紫外光照射70 min时MB脱色率达98.32%。g-C_3N_4催化剂具有较好的重复使用性能,使用5次后MB脱色率仍保持在95.10%。     

除镉最佳混凝剂的筛选及应用条件研究

通过采用聚合氯化铝铁（PAFC）、氯化铁（FeCl3）及聚合硫酸铁（PFS）对含镉废水的处理研究表明,三种混凝剂对含镉水体均有良好的处理效果,同等条件下,三种混凝剂对含镉水体去除率分别为98.22%、92.19%和93.63%。研究了PAFC对含镉水体的混凝沉淀效果,实验结果表明：碱性条件有利于镉离子的沉淀,当pH为9～11时,去除率可达98.00%左右;对于初始浓度为4.000 0 mg.L-1的含镉废水,经处理后,水体浓度可降至0.184 0 mg.L-1,对于初始浓度为0.400 0 mg.L-1的含镉废水,经处理后水体浓度降至0.007 2 mg.L-1;废水中投加一定量的石灰乳对PAFC除镉起一定的作用,投加量达30.00 mg.L-1时,其去除率达99.91%;通过对PAFC除镉动力学拟合,符合一级线性动力学方程。     

改性人造沸石处理含黄玉铬洁(Ⅵ张焕)祯地下水的实验研究

为了提高人造沸石对地下水中铬(Ⅵ)的去除能力,采用氯化铝对人造沸石进行改性。确定最佳改性条件:20%氯化铝溶液,液固比12 mL/g,室温下以180 r/min振荡改性8 h;最佳除Cr(Ⅵ)条件:pH值为4～8,液固比为33.3 mL/g,室温下水浴恒温振荡2 h。改性沸石对铬(Ⅵ)的吸附符合Langmuir及Freundlich等温线方程,由Langmuir吸附等温线可得其吸附容量为5.624 mg/g。在最佳反应条件下,水样中铬(Ⅵ)浓度可由5 mg/L下降到0.026 mg/L,低于0.05 mg/L,满足GB/T 14848—93《地下水环境质量标准》Ⅲ类标准。     

氧气热处理的TiO2纳米管阵列光电催化降解亚甲基蓝的研究

采用原位阳极氧化法在Ti基底上制备了高度有序的TiO2纳米管阵列薄膜,SEM图像表明TiO2纳米管定向排列整齐,分布均匀,其管径范围在70～100 nm.XRD结果证明,阳极氧化法制备的TiO2纳米管为无定型晶型,经退火后为具有良好光催化活性的锐钛矿型.以亚甲基蓝（methylene blue）为目标物研究了TiO2纳米管光电催化性能及影响因素,结果表明,以0.1 mol/L NaCl为电解质,在氧气热处理气氛下,外加偏压为0.5 V、pH=3.25、光照强度为1 000μW/cm2、纳米管薄膜表面积为2 cm×2 cm且MB初始浓度为10 mg/L的条件下,TiO2纳米管阵列薄膜光电催化降解MB的降解效率可达99.56%.电化学阻抗谱分析显示,光电催化降解过程的速控步骤均为表面反应步骤,外加偏压减小了界面电荷转移阻抗,提高了光生载流子的分离效率.     

Cu(NO3)2在亚甲蓝湿式氧化处理中的应用

用CWAO技术处理COD为2 000 mg/L的亚甲蓝水溶液.以Cu(NO3)2为催化剂,考察了催化剂投加量、反应温度、压力及进水pH值对亚甲蓝水样COD去除率、脱色率、出水pH值的影响.实验表明,亚甲蓝的氧化效率随催化剂投加量的增加,反应温度及压力的升高而升高.然而,综合考虑亚甲蓝的氧化效率、试剂费用、设备成本及能量消耗,实验确定Cu(NO3)2的投加量以Cu2 计为150 mg/L,反应温度及压力分别为200℃和2.0 MPa.在酸性进水条件下,COD去除率随进水pH值的降低而升高;而在碱性进水条件下,COD去除率随进水pH值的升高而升高.pH值按COD去除率由高到低的排列顺序是:3.87、11.23、5.50、7.25、9.47,实验确定最佳进水pH值是3.87.在以上最佳的操作条件下,反应150 min,水样COD去除率达97.4%,脱色率达99.97%,出水pH值3.63.     

Metal chlorides loaded on activated carbon to capture elemental mercury

Activated carbon (AC) was considered to be an effective sorbent to control mercury in combustion systems. However, its capture capacity was low and it required a high carbon-to-mercury mass ratio. AC loaded with catalyst showed a high elemental mercury (Hg0) capture capacity due to large surface area of AC and high oxidization ability of catalyst. In this study, several metal chlorides and metal oxides were used to promote the sorption capacity of AC. As a result, metal chlorides were better than metal oxides loaded on AC to remove gaseous mercury. X-ray diffractometer (XRD), thermogravimetric analyzer (TGA) and specific surface area by Brunauer- Emmett-Teller method (BET) analysis showed the main mechanisms: first, AC had an enormous surface area for loading enough MClx; second, Cl and MxOy were generated during pyrogenation of MClx; finally, there were lots of active elements such as Cl and MxOy which could react with elemental mercury and convert it to mercury oxide and mercury chloride. The HgO and HgCl2 might be released from AC’s porous structure by thermo regeneration. A catalytic chemisorption mechanism predominates the sorption process of elemental mercury. As Co and Mn were valence variable metal elements, their catalytic effect on Hg0 oxidization may accelerate both oxidation and halogenation of Hg0. The sorbents loaded with metal chlorides possessed a synergistic function of catalytic effect of valence variable metal and chlorine oxidation.